Typical properties of some formulations
  
Formula Hardness Tensile Strength Elongation At Break Modulus Tear Strength
  SHD MPa % Mpa kN/m
      
SA30 30°A 10.6 500 1.5 —
SA50 50°A 20.6 500 2.8 —
SA60 60°A 26.2 420 5 36
SA70 70°A 33.8 420 5.1 58
SA85 85°A 45 580 8 —
SA90 90°A 46.1 520 13.7 91
EA80 80°A 26.5 480 9.1 58
EA90 90°A 34 430 13.5 78
EA95 95°A 40.2 400 22.3 103
ED60 60°D 51 300 51 —
ED75 75°D 70.6 270 — —
  A comparasion of polyurethanes with other materials  
Legend:
Y = Better than 
O = Equal to  
X = Not as good 
Property
Natural
Chloroprene
Nitrile
Butyl
C.S.M
Silicone
Polysulphide
 
Rubber and SBR
 
 
 
 
 
 
 
 
 
 
 
 
 
 
Tensile Strength
Y
Y
Y
Y
Y
Y
Y
Elongation at high hardness
Y
Y
Y
Y
Y
Y
Y
Abrasion Resistance
Y
Y
Y
Y
Y
Y
O
Resilience
O
O
O
Y
O
O
Y
Tear resistance
Y
Y
Y
Y
Y
Y
Y
Cut Growth
Y
Y
Y
Y
Y
Y
Y
Compression Set
O
Y
Y
Y
Y
Y
Y
Impact Resistance
Y
Y
Y
Y
Y
Y
Y
Load Capacity
Y
Y
Y
Y
Y
Y
Y
Weather and Ozone Resistance
Y
Y
Y
O
O
O
Y
Heat Resistance
O
X
O
X
X
X
Y
Low Temp. Flexibility
Y
Y
Y
Y
Y
O
Y
Electrical Properties
O
O
O
O
O
X
Y
Acid Properties
O
O
O
X
X
O
Y
Water Resistance
O
Y
Y
Y
Y
Y
Y
Oil and Solvent Resistance
Y
Y
Y
Y
Y
Y
Y